*HEADING
CAST IRON PLASTICITY, COUPLED TEMPERATURE DISPLACEMENT, CAX4T
*NODE,NSET=ALL
1,
2,.01,0.
3,.01,.01
4,0. ,.01
*ELEMENT,TYPE=CAX4T,ELSET=METAL
1, 1,2,3,4
*Distribution Table, name=distTableElastic
 modulus, ratio
*Distribution, name=distElastic, table=distTableElastic, location=element
 , 1.0, 0.0
 METAL,14.773E6,0.2273
*SOLID SECTION,ELSET=METAL,MATERIAL=EL
*MATERIAL,NAME=EL
*ELASTIC
distElastic,
*CAST IRON PLASTICITY
0.039, 
*CAST IRON TENSION HARDENING
10.125E+03,0.000E+00,,0.
19.50E+03,3.154E-04,,0.
26.10E+03,8.686E-04,,0.
32.00E+03,1.719E-03,,0.
34.50E+03,2.550E-03,,0.
6.125E+03,0.000E+00,,600.
15.50E+03,3.154E-04,,600.
22.10E+03,8.686E-04,,600.
28.00E+03,1.719E-03,,600.
30.50E+03,2.550E-03,,600.
*CAST IRON COMPRESSION HARDENING
32.00E+03,0.000E+00,,0.
55.12E+03,2.404E-03,,0.
67.60E+03,6.559E-03,,0.
74.50E+03,11.092E-03,,0.
78.90E+03,13.795E-03,,0.
28.00E+03,0.000E+00,,600.
51.12E+03,2.404E-03,,600.
63.60E+03,6.559E-03,,600.
70.50E+03,11.092E-03,,600.
74.90E+03,13.795E-03,,600.
*EXPANSION
11.E-06, 
*CONDUCTIVITY
9.4, 
*SPECIFIC HEAT
47.52, 
*DENSITY
439.92, 
*INITIAL CONDITIONS,TYPE=TEMPERATURE
ALL,0
*BOUNDARY
1, 1,2
2, 2,2
4, 1,1
*STEP,INC=100,AMP=RAMP
*COUPLED TEMPERATURE-DISPLACEMENT,DELTMX=60.
1.E-03,1.
*BOUNDARY
3,11,11,600.
4,11,11,600.
*DLOAD
METAL,P3,-30.E+03
*EL PRINT, ELSET=METAL,FREQUENCY=10
S,MISES
E, 
PE, 
PEEQT, 
TEMP, 
*NODE PRINT, FREQUENCY=10
U,RF,NT,RFL
*OUTPUT,FIELD,FREQ=10
*ELEMENT OUTPUT
S,E,PE
PEEQT,
TEMP,
*OUTPUT,FIELD,FREQ=10
*NODE OUTPUT
U,
RF,
NT,
RFL,
*END STEP